Columns are the structural members of buildings that ensure structural stability. A fire can severely affect the columns' structural performance by degrading the properties of their constituent materials, thereby reducing the strength capacity, stiffness, and stability. In seismic zones, the knowledge of the post-fire behavior of these elements is a fundamental requirement for a realistic seismic performance assessment. This study utilized numerical analysis using the parametric fire model of Eurocode-1 to estimate the post-fire axial and lateral performance of reinforced concrete columns. In the first step, the axial load-bearing capacity was evaluated from a parametric study for cantilever columns. In the second step, the lateral load capacity, force-displacement behavior, stiffness, ductility, energy dissipation capacity, and residual displacements were estimated to determine the impact of fire damage on the behavior of columns under lateral loads. The results showed that both the lateral load capacity and the ductility of the reinforced concrete columns decreased significantly due to fire exposure. This also indicated that fire damage decreases the vertical load-bearing capacity, and the reduction in lateral capacity was attributed to the loss of concrete's compressive strength. The column characteristics that significantly influence the residual response behavior were identified as section size, column height, axial load ratio, and concrete's compressive strength.

The paper aims to study cellular concrete with a new approach of formulation without an autoclave, with the use of aluminum waste and incorporation of mineral additions into the sand and evaluate its physical and mechanical properties. In this experimental study, two types of cellular concrete are prepared, based on crushed and dune sand with the incorporation of 15% of the slag and 10% of pozzolana, as sand replacement. An experimental program was performed to determine the compressive strength at 28 days, the density and thermal conductivity of the confected cellular concrete. The obtained results showed that concretes prepared with crushed sand developed better mechanical resistance compared to the dune sand. It is also noted that the concretes containing the mineral additions provide a substantial increase in compressive strength in particular slag. Furthermore, cellular concretes with sand dunes offer better thermal conductivity, compared to those with crushed sand. The use of the additions reduces the Water/Binder (W/B) ratio and leads to a lower thermal conductivity regardless of the used sand nature. The outcome of the present study here in could present a modest contribution for the production of cellular concrete with local materials in particular dune sand, active mineral addition and aluminum waste. The physical and mechanical properties obtained from this new composition are estimated acceptable compared to those of the industry-prepared cellular concrete product.

This paper presents a study of the behaviour of Reinforced Concrete (RC) slabs subjected to severe hydrocarbon fire exposure. In which the spalling phenomena of concrete is to be considered. The hydrocarbon curve is applicable where small petroleum fires might occur, i.e. car fuel tanks, petrol or oil tankers, certain petro-chemical facilities, tunnels, parking structures, etc. Spalling is included using a simplified approach where elements with temperatures higher than 400 °C are assumed to occur and the corresponding thermo-mechanical response of RC slabs is evaluated. The nonlinear finite element software SAFIR has been used to perform a numerical analysis of the spalling risk, by removing layers of concrete covering when a set of spalling criteria is checked. The numerical results obtained by finite element analysis of the temperature distribution within the slab and mid-span deflection were compared with published experimental data. Predictions from the numerical model show a good agreement with the experimental data throughout the entire fire exposure to the hydrocarbon fire. This shows that this approach (layering procedure) is very useful in predicting the behaviour of concrete spalling cases.

 To evaluate the performance of concrete load bearing walls in a structure under horizontal loads after being exposed to real fire, two steps were followed. In the first step, an experimental study was performed on the thermo-mechanical properties of concrete after heating to temperatures of 200-1000oC with the purpose of determining the residual mechanical properties after cooling. The temperature was increased in line with natural fire curve in an electric furnace. The peak temperature was maintained for a period of 1.5 hour and then allowed to cool gradually in air at room temperature. All specimens were made from calcareous aggregate to be used for determining the residual properties: compressive strength, static and dynamic elasticity modulus by means of UPV test, including the mass loss. The concrete residual compressive strength and elastic modulus values were compared with those calculated from Eurocode and other analytical models from other studies, and were found to be satisfactory. In the second step, experimental analysis results were then implemented into structural numerical analysis to predict the post-fire load-bearing capacity response of the walls under vertical and horizontal loads. The parameters considered in this analysis were the effective height, the thickness of the wall, various support conditions and the residual strength of concrete. The results indicate that fire damage does not significantly affect the lateral capacity and stiffness of reinforced walls for temperature fires up to 400oC.

This paper presents an experimental study to evaluate the effect of local mineral additions (pozzolan, slag and limestone) on the rheological behaviour of based cement binder’s pastes. The binary, ternary and quaternary binder pastes were prepared with the partial clinker cement replacement limited up to 20%, according with type CEM II specifications. The cements were characterized by their geometric shapes, the reactivity and the chemical composition. An experimental design plan was used to modelling the rheological behaviour of pastes. The relatives yield stress and plastic viscosity of binder’s pastes, with normal consistency, were determined. The results showed that all the tested compositions with additions follow the same rheological behaviour law according to the Bingham model. The binder pastes rheological parameters (yield stress and viscosity) are affected by mineral additions. The highest values of the rheological parameters were measured in binary and ternary cements with limestone and pozzolan. On the other hand, the lower viscosity among the tested pastes was obtained with slag addition. The statistical approach allowed us to obtain a satisfactory modelling of viscosity and yield stress with a coefficient of determination R² = 0.91 and 0.92, respectively and a satisfactory correlation between the viscosity and the water/binder ratio (W/B) for a normal consistency with a coefficient of determination R² = 0.91.

Sand occupies a great proportion of the cementitious matrix product and in particular mortars. Hence, the study of fine aggregates used for concrete and mortar in general, deserves to be objects of research including sand which has always been considered as inert material, whose role is exclusively physical. The study of mortars performances based on prepared sand to assess the effect of the type and rate of substitution of mineral additions pozzolana and blast furnace slag of a natural sand fine fraction (sieve diameter less than 0.16 mm) is seen as the main objective of the present experimental research work. The natural sand replaced size is less than 160 µm and for rheological reasons the maximum replacement rate of natural sand is limited to 10%. The results obtained show a significant improvement of the mechanical properties for the mortars based on the new activated sand. With regard to durability tests of HCl and H2SO4 acids chemical attacks, the substitution of the quartz by active mineral additions in the sand-size skeleton allows an advantageous reduction in loss of resistance up to 50% and a mass gain around 75%.